[anyz]

Hi,
I'm looking for tin (Sn) powder at home lab. is there a simple way like heating and getting it i powder form possible mixing some other substance.

and finally what is its final color; gray , white?

[billnotgatez]

abrasion or grinding?

As a side note
since you are new
you might look at the forum rules if you have not done so already
Click on the link near the top center of the forum page.
Forum Rules: Read This Before Posting.

By the way you will find interesting reading at
https://en.wikipedia.org/wiki/Tin

[anyz]

Sure i'm looking more closely on these now

[Intanjir]

Melt it and use a plunger to spray it out of a small nozzle? Your oven could melt it.

Or just file it... it is quite soft.

[Arkcon]

A pure metal is unlikely to be white, that sounds like an oxide to me.  Tin does exist in a allotropic form called tin pest or tin disease, but the best way to achieve it is very low temperatures.  Generally that, for whatever application you have planned, its best to just purchase it.

[anyz]

Let me give some background. I'm looking to powder the Tin for making its Calyx that is traditional indian way for making medicine by mixing with other herbs.

- Metal should be in pure powder form without any grain/particles
Traditional ways recommended are by heating with alum or similar stuff. But this is also not fully documented.

 Further as available in market tin powder color is pure white but i could not get that color even while using documented methods. Its always graish.

[Intanjir]

Tin is a relatively bright metal, so bright that we refer to it as a white metal, however all metals absorb enough light that their powders will always be a least somewhat grey. Tin is light grey.
Oxides on the other hand are very often very clear and thus totally white when finely powdered as they absorb very little light. Tin oxide is white.

If the powder is white then it isn't pure tin metal.
From what I googled just now traditional Indian medicine had a very different conception of 'purification' than modern Western chemistry. They start with the already pure metal and grind and calcine it with all sorts of herbs over and over again and end up with an impure metal oxide and then identify this product as the 'pure metal'. I suppose this could be intended as some kind of spiritual purity or just a simple physical misunderstanding or some combination.

BTW, until around 1780 Western chemists would have agreed. The Indians would have been seen as making dephlogisticated tin, ie removing the phlogistan from tin thus purifying it.

Anyways if the market is selling a traditional 'purified tin' product and it is white then this all makes sense.

Now you aren't going to get a metallic tin powder by heating it with alum or herbs. You very well could get a substantially tin oxide powder by melting the tin with who knows what and crush and grind from there. It is certainly much easier to powder a brittle, crushable oxide. Potassium Alum might be able to hold on to its tightly bound waters of hydration long enough to provide water to molten tin to begin to oxidize it.

As long as you have grey you probably still have some metallic tin present. I imagine you will have to repeatedly crush and calcine it before you get rid of enough for it to be completely white.

Here is a paper that argues that such traditional methods make nano-scale tin oxide:

http://article.sciencepublishinggroup.com/pdf/10.11648.j.nano.20140204.13.pdf